Lets face it, nobody likes to replace filters.  That’s why nTEX medias feature our unique PulseFlex polymer that can withstand extended abuse with the most challenging dusts. The proprietary flexible nanofiber surface provides low initial & operating pressure drop, excellent dust release, and long service life.  nTEX industrial medias are available in efficiencies from MERV 12-16 on synthetic or cellulose blend bases.

nTEX NP003 - F9 Synthetic Filter Media

  

NP003 Specifications at a Glance

  • Construction: Nanofiber over polyester nonwoven (pulsable surface filtration)
  • Efficiency: F9 / MERV 15 
  • Air Permeability:
    • 30 ft3/min/ft2 (cfm) @ 0.5”H2O (ASTM D737) U.S.
    • 140 l/dm2/min @ 200Pa  (DIN 53887) Germany
    • 15 cm3/cm2/s @ 125Pa  (JIS L 1096 A) Japan 
  • Basis Weight: 120 GSM
  • Finish: Standard
  • Available Widths: 25.9 – 82.0 inches (657 – 2030 mm)
  • Process Data: Designed for rotary pleating - pre & post heat recommended

Download detail specs

nTEX NC010 - F8 Cellulose Blended Filter Media
NP010 Specifications at a Glance
  • Construction: Nanofiber over polyester nonwoven (pulsable surface filtration)
  • Efficiency: E-10
  • Air Permeability:
    • 14 ft3/min/ft2 (cfm) @ 0.5”H2O (ASTM D737) U.S.
    • 65 l/dm2/min @ 200Pa  (DIN 53887) Germany
    • 7 cm3/cm2/s @ 125Pa  (JIS L 1096 A) Japan
  • Basis Weight: 130 GSM
  • Finish: Standard
  • Available Widths: 25.9 – 82.0 inches (657 – 2030 mm)
  • Process Data: Designed for rotary pleating - pre & post heat recommended
Download detail specs
nTEX NC004 - F9 Cellulose Blended Filter Media

NC004 Specifications at a Glance

  • Construction: Nanofiber over cellulose/poly blend (pulsable surface filtration)
    • Efficiency: MERV 15
    • Oil rating >7 AATCC - 118
  • Hydrostatic Head > 20 Mbar @ 20 mbar/min Ref. AATCC - 127
  • Air Permeability:
    • 20 ft3/min/ft2 (cfm) @ 0.5” H2O (ASTM D737) U.S
    • 96 l/dm2/min @ 200Pa (DIN 53887) Germany
    • 10 cm3/cm2/s @ 125Pa (JIS L 1096 A) Japan
  • Basis Weight: 122 GSM
  • Finish: xPEL treated & Fire Retardant
  • Available Widths: 25.9 – 80.0 inches (657 – 2030 mm)
  • Process Data: Designed for rotary pleating
nTEX NP002 - F9 Synthetic Filter Media – Hydrophobic Treated

NP002 Specifications at a Glance

  • Construction: Nanofiber over polyester nonwoven (pulsable surface filtration)
  • Efficiency: F9 / MERV 15
    • Oil rating >7 AATCC - 118
    • Hydrostatic Head > 30 Mbar @ 20 mbar/min Ref. AATCC - 127
  • Air Permeability:
    • 30 ft3/min/ft2 (cfm) @ 0.5”H2O (ASTM D737) U.S.
    • 140 l/dm2/min @ 200Pa  (DIN 53887) Germany
    • 15 cm3/cm2/s @ 125Pa  (JIS L 1096 A) Japan
  • Basis Weight: 130 GSM
  • Finish: Standard
  • Available Widths: 25.9 – 82.0 inches (657 – 2030 mm)
  • Process Data: Designed for rotary pleating – pre & post heat recommended

Download detail specs

nTEX NC015 - F9 Cellulose Blended Filter Media

NC015 Specifications at a Glance

  • Construction: Nanofiber over cellulose/poly blend (pulsable surface filtration)
  • Efficiency: F9 / MERV 15
    • Oil rating >7 AATCC - 118
    • Hydrostatic Head > 20 Mbar @ 20 mbar/min Ref. AATCC - 127
  • Air Permeability:
    • 20 ft3/min/ft2 (cfm) @ 0.5” H2O (ASTM D737) U.S.
    • 96 l/dm2/min @ 200Pa (DIN 53887) Germany
    • 10 cm3/cm2/s @ 125Pa (JIS L 1096 A) Japan 
  • Basis Weight: 122 GSM
  • Finish: xPEL treated Super Hydro/Oleophobic
  • Available Widths: 25.9 – 80.0 inches (657 – 2030 mm)

Process Data: Designed for rotary pleating

Download detail specs

nTEX NC007 - F9 Cellulose Blended Filter Media

NC007 Specifications at a Glance

  • Construction: Nanofiber over cellulose/poly blend (pulsable surface filtration)
  • Efficiency: MERV 15
  • Air Permeability:
  • 20 ft3/min/ft2 (cfm) @ 0.5”H2O (ASTM D737) U.S.
  • 96 l/dm2/min @ 200Pa  (DIN 53887) Germany
  • 10 cm3/cm2/s @ 125Pa  (JIS L 1096 A) Japan
  • Basis Weight: 122 GSM
  • Finish: Fire Retardant
  • Available Widths: 25.9 – 80.0 inches (657 – 2030 mm)
  • Process Data: Designed for rotary pleating

Download detail specs